Ekstrak Daun Matoa (Pometia pinnata) sebagai Inhibitor Korosi Baja Karbon SS-304

Renny Fitria, Dahyunir Dahlan, Syukri Syukri

Abstract


Research has been carried out on inhibitors from matoa leaf extract to inhibit the corrosion rate of SS-304 carbon steel. The Matao leaf extract used as an inhibitor was immersed in a 1 M H2SO4 corrosive medium. To determine the effect of inhibitor concentration and immersion temperature on steel corrosion, various inhibitor concentrations were varied, namely 0%, 1%, 2%, and 3% bt, and temperature variations, namely samples also in XRD and SEM characterization. 35°C and 40°C. The corrosion rate test was carried out using the weight loss method. The increase in the corrosion rate is in line with the increase in sample weight loss. The most efficient inhibitor of matoa leaf extract was obtained at a concentration of 3% with an immersion temperature of 35°C, namely 0.09 mmpy. The XRD results showed that the maximum peaks produced FeC and FeNi crystals, followed by FeO crystals. SEM characterization also showed that samples without inhibitors were more corroded, and samples using 3% inhibitor concentrations were slightly corroded.


Full Text:

PDF

References


Tretheway, Kr., Chamberlain J. 1991. Korosi untuk Mahasiswa dan Rekayasawan. Jakarta: PT. Gramedia Pustaka Utama.

Nugroho, F., 2015, Penggunaan inhibitor untuk meningkatkan ketahanan korosi pada baja karbon rendah. Jurnal Angkasa, 7(1), 151–158.

Hakimin, Afifah Z., 2021, Sintesis Lapisan Antikorosi Menggunakan Ekstrak Daun Ketapang (Terminalian catappa L) sebagai Inhibitor Korosi pada Baja. Diploma thesis, Universitas Andalas.

Hartono, R., 2021, Ekstrak Daun Jarak Sebagai Inhibitor (Penghambat) Korosi pada Baja Karbon, Dinamika Jurnal Teknik Mesin Unkhair, Volume 6, Nomor 1.

Rima, R.F., 2018, Inhibitor Korosi Baja Ramah Lingkungan dari Ekstrak Daun Matoa (Pometia pinnata) dalam Medium Asam . Tesis, Jurnal Riset Kimia Vol 5 No. 2, Jurusan Fisika, Universitas Andalas Padang

Mardhani, I., & Harmami. 2013. Pengaruh Suhu Terhadap Korosi Baja SS 304 dalam Media 1 M HCL dengan Adanya Inhibitor Kinina. Jurnal Sains Dan Seni Pomits. Vol 2. No 2. pp 2–4.

Variany, G., 1999, Isolasi dan Identifikasi Flavonoid Dari Daun Pometia pinnata J.R&G.Forst; Skripsi, Fakultas Farmasi; Universitas Tanjung Pura, Pontianak.

Dayana, M., 2014. Studi Pengaruh Penambahan Konsentrasi Ekstrak Ubi Jalar Ung (Ipomeae batatas Poiret) Sebagai Green Inhibitor Terhadap Laju Korosi Pada Baja API 5L GRADE B Schedule 40 di Lingkungan NaCl 3,5%. Diploma Thesis. Universitas Andalas

Takahashi Y, Matsubara E, Suzuki S, Okomoto Y, Komatsu t, Konishi H, Mizuki J and Waseda Y, 2005, In-situ X-ray Diffraction of Corrosion Product Formed on Iron Surfaces, Materials Transactions, 46 (3), 637-642.

HSBR, P., 2012, Karakteristik Morfologi Permukaan dan Sifat Magnetik NiFe Hasil Elektrodeposisi, Skripsi, Universitas Sebelas Maret,Surakarta.

Yufita, Fitrianna, Zulfalina, 2018, Pengendalian Laju Korosi Pada Baja Plat Hitam A36 Dalam Medium Korosif Menggunakan Inhibitor Daun Salam, Jurnal Aceh Phys.Soc Vol.7, No.2 pp. 67-71. Jurusan Fisika Fakultas MIPA, Universitas Syiah Kuala.




DOI: https://doi.org/10.25077/jfu.13.1.49-53.2024

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License

Published by:

Departemen Fisika, FMIPA Universitas Andalas

Kampus Unand Limau Manis Padang Sumatera Barat 25163

Telepon 0751-73307

Email:jfu@sci.unand.ac.id