PENGARUH SUHU PADA PROSES SONIKASI TERHADAP MORFOLOGI PARTIKEL DAN KRISTALINITAS NANOPARTIKEL Fe3O4
Abstract
ABSTRAK
Penelitian mengenai pengaruh suhu pada proses sonikasi terhadap morfologi partikel dan kristalinitas nanopartikel Fe3O4 disintesis dengan metode kopresipitasi-sonikasi telah dilakukan. Nanopartikel magnetik disintesis dari batuan besi dengan metode kopresipitasi yang ditambahkan polietilen glikol (PEG-6000) dengan perbandingan massa 1 : 5. Sampel selanjutnya disonikasi dengan variasi suhu sonikasi 500C, 600C, dan 650C. Ukuran kristal, dan distribusi diameter partikel dari nanopartikel ini dikarakterisasi menggunakan X-Ray Diffractometer (XRD), dan Scanning Electron Microscope (SEM). Dari hasil analisis pola difraksi sinar-x terdapat dua struktur yaitu kubik spinel dari magnetit (Fe3O4) dan heksagonal dari hematit (Fe2O3). Ukuran kristal semua sampel berkisar antara 93 nm - 110 nm dan ukuran partikel semua sampel berkisar antara 25 nm - 200 nm. Hasil SEM menunjukkan semakin tinggi suhu sonikasi, morfologi semua sampel semakin homogen dan rongga pemisah antara partikel lebih kecil.
Kata kunci: Nanopartikel magnetik, kopresipitasi, PEG-6000, sonikasi
ABSTRACT
The research is about the effect of temperature on the process of sonication on particle morphology and crystallinity of Fe3O4 nanoparticles synthesized by coprecipitation-sonication method. Magnetic nanoparticle was synthesized from loadstone using coprecipitation method with addition of polyethylene glycol (PEG-6000) with comparison of mass i.e 1 : 5. The sample was sonicated with various of temperature 500C, 600C, and 650C. X-ray patterns analysis, show that two structures that are cubic spinel of magnetite (Fe3O4) and hexagonal of hematite (Fe2O3). The crystallite size of all samples are approximately from 93 nm - 110 nm. The particle size of all samples are approximately from 25 nm - 200 nm. The SEM images that higher of temperature sonication, morphology of all samples are semispherical shape and separation cavity of between particles are smaller.
Keywords: magnetic nanoparticles, coprecipitation, PEG-6000, sonication
Full Text:
PDFDOI: https://doi.org/10.25077/jfu.4.1.%25p.2015
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License
Published by:
Departemen Fisika, FMIPA Universitas Andalas
Kampus Unand Limau Manis Padang Sumatera Barat 25163
Telepon 0751-73307
Email:jfu@sci.unand.ac.id